Abstract
Combined with converter semi-steel component of Chengde steel plant, the main components of 100t ladle dephosphorization slag were calculated to propose the initial ratio of dephosphorization slag composition. The dephosphorization slag composition was then further improved by induction furnace dephosphorization. Analysis of dephosphorization rules has been done. The results show that: the dephosphorization effect reaches the best when the percent content of CaO is 35%, the amount of slag is 20kg/t, oxygen flow rate is 4L/min, oxygen blowing time is 4min, and dephosphorization efficiency can reach 56.9%; the order of the elements influencing dephosphorization rate is as follows: oxygen flow rate > slag > CaO > oxygen blowing time. From the experiment, dephosphorization in the ladle can reach the expected effect, which is the new method of hot metal pre-dephosphorization for iron and steel plant using vanadium titanium magnetite.
Publisher
Trans Tech Publications, Ltd.
Reference10 articles.
1. Singh BN. Recent fiends in iron and steelmaking technology[J]. Bulletin of Materials Science, 1 989, 1 2(3): 435-447.
2. Ueda T，Marukawa K Shirota Y．Sumitomo'S SARP(Sumitomo Alkali Refining or Slag All Recycling)Process[J]．Steel Times Int, 1985, 9(1): 46.
3. Hikosaka A．Kinetic Study on Dcphosphorization of Hot Metal by Lime·Based Flux Injection in Different Vessels. 1 985: 285—292.
4. Nakajima Y，Fukami Y，Moriya T，Maruhashi S．A New Injection Process for Dephosphorization of Hot Metal. 1 989: 469—477.
5. Ohji M．Production and Technology of Iron and Steel in Japan during 1 999[J]. ISIJ international, 2000, 40(6): 529-543.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献