Grain Refinement of Pure Copper by ECAP

Abstract

Pure commercial Cu of 99,98 wt % purity was processed at room temperature by Equal- Channel Angular Pressing (ECAP) following route Bc. Heavy deformation was introduced in the samples after a considerable number of ECAP passes, namely 1, 4, 8, 12 and 16. A significant grain refinement was observed by transmission electron microscopy (TEM). Tensile and microhardness tests were also carried out on the deformed material in order to correlate microstructure and mechanical properties. Microhardness measurements displayed a quite homogeneous strain distribution. The most significative microstructural and mechanical changes were introduced in the first ECAP pass although a gradual increment in strength and a slight further grain refinement was noticed in the consecutive ECAP passes.