Laser Cladding Cermet Coatings on Niobium Substrate

Abstract

Pure niobium substrates were coated using laser cladding method. Pure molybdenum, Yttria Stabilized Zirkonia (YSZ) and corundum (Al2O3) powders were used as coating materials. Coatings were deposited on specimens as seperate paths with 3÷10mm width and 40mm of length. Two different laser power 3kW and 4kW were tested during deposition. In order to assess the quality of the Mo-YSZ and Mo-Al2O3 coatings, the light microscopy, Scanning Electron Microscopy (SEM), chemical analysis (EDS) and Vickers hardness test investigation were performed. The surface roughness and wear volume were also measured. As a result of YSZ-Mo powder cladding on the Nb substrate the composite layers were obtained without cracks and porosity not exceeding 1 μm. In addition, an increase in hardness of about 450 HV0.5 was revealed. As a result of Al2O3-Mo powder cladding on the Nb substrate the composite layers with many voids and cracks were obtained for each of the cladding variants.