The cold draw MFT8 steels with different reduction in cross sectional areas were investigated to understand the effect of aging time on the anti-stress relaxation ability of non-quenched and tempered steel. The hardness and the anti-stress relaxation ability of cold draw NQT MFT8 steel was improved after aging at 300°Csince the precipitation of submicron particles within deformed ferrite. The cold draw NQT MFT8 becomes harder and more resistant to stress relaxation with increasing aging time. The cold draw MFT8 with both 25% and 30% reduction in cross sectional areas are stress relaxation resistant after aged at 300°C for 2 hours.
Publisher
Trans Tech Publications, Ltd.
Reference8 articles.
1. Z.T. Han, N.J. Zhang, D. Gao and G. Yang: J. China Univer. Mining & Tech. Vol. 17 (2007), p.0238.
2. L. Yi, J.M. Peng, H.B. Wang and X.C. Wu: Mater. Sci. Eng. A Vol. 527( 2010), p.3433.
3. S.R. Humphries, K.U. Snowden and W. Yeung: Mater. Sci. Eng. A Vol. 527( 2010), p.3240.
4. E. J. Hearn: Mechanics of Materials 2 (Butterworth-Heinemann, Eastbourne 2001).
5. L. Cai, X.M. Zhao and X.C. He: Iron and Steel Vol. 45(2010), p.75.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献