Abstract
The cyclic oxidation behavior of Co-10Cr-5Si alloys with and without Y in atmosphere at 800 °C was investigated. The addition of 0.3 at.% Y decreased the average parabolic rate constant from 4.45×10-10g2cm-2s-1to 3.58×10-10g2cm-2s-1. The thin scales grown on Co-10Cr-5Si alloys were mainly composed of an outer CoO layer, followed by an inner protective SiO2layer. However, the scales can not be observed for Co-10Cr-5Si-0.3Y alloy, probably due to the spallation of the scales during the cooling process. The addition of 0.3 at.% Y improved the cyclic oxidation resistance of the Co-10Cr-5Al alloy.