Abstract
By plasma cladding technology, the Ni60B/TiC composite coating metallurgically bonded to Q235 steel were prepared using Ni-based alloy and TiC powders. The microstructure formation mechanism of the clad layers was investigated by scanning electron microscopy (SEM) and X-ray Diffraction (XRD). The microhardness distribution and wear resistance of the specimens were tested. The results show that metallurgical combination is achieved between coating and substrate, the microstructure of composite coating is composed of dendrite γ-Ni, α-Fe, added TiC and FeNi. The hardness and wear resistance of composite coating have relationship with TiC particles content and TiC particles distribution. The hardness and wear resistance increase with the increase of TiC particles content.
Publisher
Trans Tech Publications, Ltd.
Reference8 articles.
1. I. Manna, J. D. Majuumdar and B. R. Chandra: Surface and Coating Technology, Vol. 201 (2006), p.434.
2. C. Navas, M. Cadenas and J. M. Cuetos: Wear, Vol. 260 (2006), p.838.
3. W. P. JIANG and U. P. Molian: Surface and Coating Technology, Vol. 135 (2001), p.139.
4. L. ZHU, J. LI and T. WU: Materials Letters, Vol. 60 (2006), p. (1956).
5. B. Y. LOU, Z. CHEN and W. J. BAI: Trans. Nonferrous Met. Soc. China, Vol. 16 (2006), p.643.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献