Affiliation:
1. Groupe de Métallurgie Structurale
Abstract
We have subjected Zr59Cu20Al10Ni8Ti3 glassy sample to internal friction thermal cycle (IFTC) measurements under various conditions involving changes in heating/cooling rate, strain amplitude and frequency. Additional low temperature internal friction peaks (ALTIFP) were found to occur with the characteristic low temperature internal friction peak (CLTIFP) observed for some glassy alloys. The ALTIFP were enhanced on heating and reduced on cooling. Their strength increase following the number of IFTC can be related to a stress concentration in some zones of the glassy structure, which is abruptly relaxed by the viscous flow creating interfaces in the glassy structure. These interfaces are likely to be formed between atomic clusters. The growth of the ALTIFP increases significantly the whole IF level (IFL) from 10-4 to 10-2 enhancing the damping capacity of the glassy sample.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference19 articles.
1. A. M. Aboki, G. Bouquet; Scripta Metal. Vol. 21 (1987), p.889.
2. A. M. Aboki, M. Harmelin, G. Bouquet, R. Portier, Scripta Metal et Mater, Vol. 24 (1990) p.1873.
3. R. Schaller in Mechanical Spectroscopy Q -1 2001 with Applications to Materials Science (Trans Tech Publications Switzerland 2001) p.621.
4. A. V. Granato, J. Alloys and Compound, 355 (2003) p.171.
5. T. A. M. Aboki, unpublished results.