The influence of the amount of Pr6O11 additions on the microstructure and electrical properties
of varistors ceramics in the ZnO-Bi2O3 system was investigated. Samples with a low level of Pr6O11
(0.1wt %) have high microstructural homogeneity, which enhances the nonlinear coefficient greatly, and
decreases the leakage current without change of voltage ratio. When the Pr6O11 content reached 7wt%, the
ZnO grain growth was restricted and the threshold voltage was improved from 275v/mm to 440v/mm.
The additive of Pr6O11 changed the process of creating spinel phase, which came from the decomposition
of pyrochlore phase. This type of small size phase has more dragging force on the ZnO crystal, which
make the whole materials more uniform and compact.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献