Abstract
A modified polyacrylamide precursor method is presented to synthesize BaSm2Ti4O12 microwave dielectric ceramics. Under an alkaline circumstance, all the cations together with the monomer and bridging agent were dispersed into a hydrous solution with the aid of chelating agent EDTA. This mixture was initiated at about 90°C, dried, calcined at 1000°C for 2hs and finally turned into well-crystallized and single-phased BaSm2Ti4O12 ceramic powder, which was modeled and sintered at 1250°C for 2hours into well-sintered ceramics. Differential thermal analysis, thermogravimetric analysis, X-ray powder diffraction and transmission electron microscope were used to characterize the process. Microwave dielectric properties measured by a resonating cavity method contain a dielectric constant (εr) about 77.0 and quality factor (Q×f) lager than 11000.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference17 articles.
1. R.L. Bolton: PhD Thesis, University of Illinois, Urbana, IL, (1968).
2. D. Kolar, Z.S. Gaberscek, D. Suvorov: Ber. Dt. Keram. Ges. Vol. 55 (1978), p.346.
3. D. Kolar, Z.S. Gaberscek, S.B. Volavsek, et al.: J. Solid State Chem. Vol. 38 (1981), p.58.
4. S. Kawashima and M. Nishida: 87 th Annual Meeting, Am. Ceram. Soc. (1985).
5. J. H. Choy, Y.S. Han, J. Ho Sohn, and M. Itoh: J. Am. Ceram. Soc. Vol. 58 (1995), p.1169.