1. Vikram Sarabhai Space Centre
Abstract
In the present paper, Haynes 214 plate of 7mm thick was welded by Gas tungsten arc welding (GTAW) in two passes. The welded plates were subjected to post-weld heat treatment such as direct aging (DA) and solution treatment + aging (STA). The aging cycle was optimized using hardness by generating isothermal aging curve. The weld tensile properties, hardness test, microscopic analysis and fractographic studies were carried out in as-welded condition and at two different post-weld heat treatment conditions. The results show a significant increase in both yield and tensile strength after post weld heat treatment.
Publisher
Trans Tech Publications, Ltd.
Reference5 articles.
1. Matthew J. Donachie, Stephen J. Donachie, Superalloys, A Technical guide, Second edition, ASM International, Ohio, March (2002).
2. John N. Dupont, John C. Lippold, Samuel D. Kiser, Welding Metallurgy and Weldability of Nickel-base Alloys, John Wiley & Sons Inc, New Jersey, (2009).
3. G.D. Janaki Ram, Effect of laves phase on mechanical properties of Inconel 718 welds. Ph. D Thesis, IIT Madras, November (2004).
4. Haynes® 214®, High temperature alloys, Information brochure, Haynes International Inc, (2008).
5. Q. Wang, D.L. Sun, Y. Na, Y. Zhou, X.L. Han, J. Wang, Effects of TIG Welding Parameters on Morphology and Mechanical Properties of Welded Joint of Ni-base Superalloy. Procedia Engineering, 2011 (10), pp.37-41.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献