Affiliation:
1. East China Normal University
2. Chinese Academy of Sciences
Abstract
Zn2SiO4:Mn2+ was synthesized via a dipping method. Stoichiometric high pure SiO2 was put
into the solution of zinc nitrate and manganese nitrate. The mixture was milled while being heated until
the water was vaporized completely. The as-received mixture was added into the ethanol, and dispersed
well, then the mixture was milled and heated to remove the ethanol thoroughly by evaporation. The
precursor were dried for several hours at 60°C, and annealed in a reducing atmosphere of active carbon at
1000°C for 4 h. As-prepared powders of Zn2SiO4:Mn2+ was tested by XRD and SEM. Its luminescent
properties were characterized by excitation and emission spectra. The results are compared with those of
Zn2SiO4:Mn2+ prepared by a general solid state reaction.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference17 articles.
1. Extended Abstract, The Fifth International Conference on the Science and Technology of Display Phosphors( San Diego, USA, 1999).
2. P.D. Rack, A. Naman, P.H. Holloway, et al: Mater. Res. Soc. Bull. Vol. 21 (1996), p.49.
3. S. Yang, C. Stoffers, F. Zhang, et al: Appl. Phys. Lett. Vol. 72 (1998), p.158.
4. R.Y. Lee, F.L. F. Zhang, J. Penczek, et al: J. Vac. Sci. Techolo. Vol. 16 (1998), p.855.
5. J. Ballato, J.S. Lewis and P.H. Holloway: Mater. Res. Soc. Bull. Vol. 29 (1999), p.51.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献