Abstract
Fe-based metal bond has been widely used in fabricating diamond tools recently since the production cost could be greatly reduced for the low price of iron. However, graphitizing elements such as Fe, Co and Ni in the matrix catalyze the transformation of diamond to graphite during high temperature sintering process, which significantly decreases the tool’s efficiency and lifetime. In this paper, Si and Ti coating were coated on diamond grits by quasi atomic layer deposition (QALD) and vacuum slow vapor deposition (VSVD) separately not only to protect diamond from erosion but also to promote the adhesion between diamond grits and the bond. Three-point bending experiment was taken to measure the bending strength of Fe-Cu-Sn-Ni based metal bond diamond blade. In comparison with uncoated diamond blade, the bending strength of coated diamond blade improves dramatically. The theoretic calculation shows that the interface bonding strength between diamond and the metal bond increases by 181.68MPa owing to the Si coating. The effect of Si and Ti coating on interface bonding between diamond and the bond under different sintering temperatures was also illuminated.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference9 articles.
1. X.P. Xu, G.Q. Zhang and H. Huang: Key Engineering Materials, Vol. 259-2 (2004), pp.26-32.
2. X.P. Xu, Q.L. Han and Y. Li: Key Engineering Materials, Vols. 291-292 (2005), pp.85-90.
3. X.P. Xu and H. Huang: Key Engineering Materials, Vols. 257-258 (2004), pp.297-302.
4. Y.H. Wang, J.B. Zang, H.X. Wang and M.Z. Wang: Key Engineering Materials, Vols. 202-203 (2001), pp.199-202.
5. Y.H. Wang, J.B. Zang, M.Z. Wang, Y. Guan and Y.Z. Zheng: Journal of Materials Processing Technology, Vol. 129 (2002), pp.369-372.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献