Affiliation:
1. Yanshan University
2. Harbin Engineering University
Abstract
The adhesion between diamond grits and the bond strongly influence the properties of diamond tools. Since diamond is covalent crystal, the high interfacial energy leads to the poor interface bonding between diamond grits and the bond. Furthermore, the sintering temperature of traditional vitrified bond is also very high because of the high refractoriness of alkalis containing in the bond, resulting in serious thermal damage to diamond grits. In this paper, a low melting point and high strength vitrified bond has been prepared mainly from borate glass, clay and lead glass. The bond is completely glassy above 850°C and the bending strength of the bond sintered at 850°C for 7 minutes is 125.7MPa with a 6.5:3.5 corundum/bond ratio. Moreover, this bond possesses good wettability with diamond abrasive from 600°C to 850°C.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference7 articles.
1. X.P. Xu, Y.B. Hong and S. Chen: Materials Science Forum, Vol. 471-472 (2004), pp.77-81.
2. X.P. Xu and Y.Q. Yu: Surface and Coatings Technology, Vol. 198 (2005) No. 1-3, pp.459-463.
3. X.P. Xu, and Y. Li: Key Engineering Materials, Vol. 259-2 (2004), pp.225-232.
4. Y.H. Wang, Y.C. Zhao, M.Z. Wang and J.B. Zang: Key Engineering Materials, Vol. 250 (2003), pp.94-98.
5. J.B. Zang, Y.H. Wang, X.H. Zhang, M.Z. Wang and Y.Z. Zheng: Key Engineering Materials, Vol. 250 (2003), pp.78-82.
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献