AlON with a composition of Al23O27N5 was prepared by hot pressing at temperatures lower
than 1900 °C. The microstructures and final properties, including both mechanical properties and optical
properties, of the sintered specimens were studied. The results showed that sintering temperature had a
great influence on the densification of specimens and could lead to very different properties, especially
the optical transmittance and the maximum infrared transmission.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference5 articles.
1. J.W. McCauley, N.D. Corbin: J. Am. Ceram. Soc. Vol. 62 (1979), p.476.
2. R.L. Gentilman: U.S. Patent 4 520 116 (1985).
3. E.A. Maguire: U.S. Patent 4 686 070 (1987).
4. J.P. Cheng, D. Agrawal, and Y.J. Zhang, et al.: J. Mater. Sci. Lett. Vol. 20 (2001), p.77.
5. D. Lepkova: Intern. Ceram. Vol. 45 (1996), p.87. Fig. 3. The SEM micrographs of polished surface of (a) specimen 1115, (b) specimen1116 and (c) specimen 1117.
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献