Electroless Fabrication of Nd-Fe-B/α-Fe Heterostructured Composite Magnets and their Magnetic Properties

Abstract

Electroless plating was used to coat Fe layers on the hard magnetic Nd-Fe-B powders to fabricate Nd-Fe-B/α-Fe heterostructured magnetic powders. The heat treatment was performed to study the property evolution of the heterostructured magnetic powders. The results show that Fe coating was oxidized to Fe2O3while drying; through the hydrogen reduction annealing, Fe2O3was reduced to α-Fe. The coercivity of the heterostructured magnetic powders increased from 111.3 kA/m (1.4 kOe) to 524.7 kA/m (6.6 kOe) after annealing at 650°C. However, the demagnetization curve of powders presents a kink due to un-ideal coupling between hard and soft magnetic phases because of the aggregation of α-Fe. The magnetization processes of the heterostructured powders transferred from the dominant nucleation mechanism to domain wall pinning mechanism after the heat treatment.