The 25%Bi2O3-30%B2O3-10%SiO2-35%ZnO (molar ratio, abbreviated as BBSZ) glass were successfully prepared by solid-phase method. The amount of BBSZ glass varied from 1wt% to 5 wt% was optimized and its effects on the sintering behavior, structure and magnetoelectric properties of the Co / Ti doped M-type barium ferrite were investigated by HP 4291B vector analysis, scanning electron microscopy (SEM) and VSM magnetometer respectively. The testing results show that the ferrite could be well sintered at 900°C with excellent performances when the 3wt% BBSZ is added. The initiative permeability and cut-off frequency are 13.5 and 800MHz, respectiveley, which suggests that this material is a candidate for application in the fabrication of chip inductors by the technology of low temperature cofired ceramics and ferrites (LTCC).
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference12 articles.
1. A. Shanmim, J. Bray, L. Roy et al. Microwave and Magnetostatic Characterization of Ferrite LTCC for Tunable and Reconfigurable SiP Application. University of Electronic Science and Tech of China. 691-694 (2010).
2. R. L. Brown, P. W. Polinski. The integration of passive components into MCM's using advanced low-temperature co-fired ceramics. Int. J. Microcirc. Electron. Packag, 328~338 (1993).
3. Micheal Richtarsic, Jack Thornron. Characterization and Optimization of LTCC for High Density Large Area MCM's. IEEE. 92~96(1998).
4. Calina Kniajer, Kentor Dechant, Drasad Apte. Low loss, low temperature cofired ceramics with higher dielectric constants for multichip modules (MCM). IEEE. Trans. Microwave. 121~128(1997).
5. Yu Ron, Kawthar A. Zaki. Low-Temperature Cofired Ceramic (LTCC) Ridge Waveguide Bandpass Chip Filters. IEEE Trans. Microwave. 2317~2322(1999).
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献