Abstract
The phase and morphology of precipitates in heat-treated Co-28Cr-6Mo-xC (x = 0.12, 0.15, 0.25, and 0.35mass%) alloys were investigated. The as-cast alloys were solution-treated in the temperature range of 1473 to 1623 K for 0 to 43.2 ks. Complete precipitate dissolution was observed in all four alloys, each of which had different carbon contents. The holding time for complete dissolution was greater for alloys with greater carbon content. The curve representing the boundary between the complete- and incomplete-dissolution conditions for each alloy is C shaped. Under the incomplete precipitate dissolution conditions of the Co-28Cr-6Mo-0.25C alloy, an M23C6 type carbide and a π-phase (M2T3X type carbide with β-Mn structure) were observed at 1548 to 1623 K, and starlike precipitates with a stripe pattern and with a dense appearance were both observed; the former comprised the M23C6 type carbide + γ-phase, and the latter was the π-phase. In contrast, only a blocky-dense M23C6 type carbide was observed at 1473 to 1523 K.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献