Abstract
The <110> grain oriented alloy was grown by zone melting directional solidification technique. The strain-stress curves of Tb0.3Dy0.7Fe2 <110> oriented alloy in different magnetic fields have been measured and the magnetic field dependence of Young’s modulus under different compressive stress has been confirmed. It is found that Young’s modulus gradually decreases with increasing the magnetic fields when the compressive stress is in the range of 15-25 MPa and changes a little in the range of 40-50 MPa. The experimental result indicates that the magnetic field has a marked effect on the Young’s modulus of the Tb0.3Dy0.7Fe2 <110> oriented alloy at a low compressive stress and its change should be considered during the design of magnetostrictive devices.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference11 articles.
1. A.G. Olabi, A. Grunwald: Mater. and Design Vol. 29 (2008), p.469.
2. B.W. Wang, L. Weng, S.Y. Li, Z.X. Zhang S.Z. Zhou, X.X. Gao, M.C. Zhang: Mater. Sci. Forum Vol. 475-479 (2005), p.2251.
3. M. Wun-Fogle, J. B. Restorff and A. E. Clark: IEEE Trans. Mag. Vol. 39(2003), p.3408.
4. A.E. Clark, H.T. Savage, and M.L. Spano: IEEE Trans. Mag. Vol. 20(1984), p.1443.
5. B. W. Wang, W. M. Huang, Y. Sun, L. Weng, W. M. Zhao, and S. Y. Cao: Proc. SPIE, Newport Beach (2007), p.64231.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献