Eddy Current Characterization of (Fe65Co35)xAl1-x Nanocrystalline Alloy Synthesized by Mechanical Alloying Process

Abstract

An investigation was conducted to explore the applicability of Eddy Current (EC) and magnetic techniques to characterize the formation and grains size variation during Mechanical Alloying (MA) and the formation of a new mixture due to the variation of crystallography parameters. The change in apparent density was attributable to the irregular particles of the metal powders. A series of Nanocrystalline (Fe65Co35)xAl1-x samples have been prepared using M.A based on planetary ball mill under several milling conditions. M.A is a non-equilibrium process for materials synthesis. The structural effects of MA of powders were investigated by X-Ray diffraction analysis, SEM, microwaves, hysteresis magnetic and Eddy Current technique. Consequently, a nanostructure alloy was obtained with an average grain size of 8 nm. Experimental results show that fine nanocrystalline alloy powders prepared by mechanical milling are very promising for microwave applications and it is suggested that Eddy current measurement technique is a useful tool for the characterization of nanocrystalline materials.