Abstract
Some physical properties (such as lattice parameter, curie temperature, ac susceptibility) of Mg1-xZnxFe2O4 (where x = 0.3,0.4,0.5,0.6) ferrites have been studied. Magnesium Zinc Ferrites was synthesized by oxalate co-precipitation method at different synthesis temperature and characterized by X-ray diffraction and far IR absorption techniques, scanning Electron microscopy .The lattice parameter were computed. The X-ray diffraction studies reveal the formations of single phase cubic spinel structure.IR absorption bands are observed around 600 cm-1 and 400 cm-1 on the tetrahedral and octahedral sites respectively. Magnetization parameters such as saturation magnetization, and magnetic moment were calculated and the results are discussed with the help of the existing theories. Saturation magnetization was found to be in the range 2 emu/gm to 8.28 emu/gm when the samples were synthesized below 100°C. The variation of A.C. susceptibility with temperature shows the existence of super paramagnetic nature. The Curie temperature was determined from the measurement of the susceptibility verses temperature. The SEM micrograph shows the uniform distribution of the particles, the average size was estimated to be 0. 350 µm.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献