Abstract
Grain-oriented 0.8(Bi1/2K1/2)TiO3-0.2BaTiO3 (BKT-BT20) ceramics were prepared by the Reactive Templated Grain Growth (RTGG) method. The BKT-BT20 ceramics sintered at 1070°C for 100 h. The grain-oriented BKT-BT20 exhibited relatively high orientation factor, F, of 0.87 and density ratio of 92%. A resistivity of textured BKT-BT20 was 1.29×1013 Ωcm. Piezoelectric strain constant, d33, and the normalized strain, d33*, of the textured BKTBT20 ceramic in the direction parallel (//) to the tape stacking direction were 117 pC/N and 243 pm/V (at 80 kV/cm), respectively.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference15 articles.
1. Y. Hiruma, R. Aoyagi, H. Nagata, and T. Takenaka：Jpn. J. Appl. Phys. 43 (2004) 7556.
2. C. F. Buhrer：J. Chem. Soc. 36.
3. (1962) 798.
4. Y. S. Sung, H. M. Lee, W. Du, H. G. Yeo, S. C. Lee, J. H. Cho, T. K. Song, and M. H. Kim：Appl. Phys. Lett. 94 (2009) 062901.
5. H. Nagata, M saitoh,Y. Hiruma, and T. Takenaka：Jpn. J. Appl. Phys. 49 (2010) 09MD08.