Abstract
The objectives of this study were to estimate the effect of the blue light cure unit on the compression force and hardness for composite resin nanoCeram at different thickness. The basic material used in this study was Ivoclar Vivadent Tetric N-Ceram Light Cured Hybrid restorative composite resin. The samples were cured by applying a (LED.F) unit Blue phase in a wavelength emission spectrum (494 NM) was used.60 disc-shaped specimens [9 mm diameter at (0.5, 1) mm thickness and 10 mm diameter at (1.5) mm thickness] were prepared using a stainless steel mold for hardness and compressive strength measurements. A composite resin was polymerized with an aid of a ( DC 5V/1A) lamp for (10, 20 and 30) sec .Three specimens were used for each group.The results were analyzed using (linear logarithmic, quadratic, linear and power) test.The different groups showed significant variability in relation, with a significant interaction between the groups.The result showed that the greater thickness more efficient for polymerization than small thickness and the long irradiation time more efficient for polymerization than short irradiation time, long irradiation time diffusion in deep portions of the sample convert to polymer and this provide good polymerization and then good mechanicalproperties.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference23 articles.
1. A. P. Ferreira, P. C. S. Júnior, E. M. Souza, R. N. Rached, S. H. Pezzin, S. Vieira, Wavelength of experimental LEDS: hardness, elastic modulus, degree of conversion and temperature rise of a microhybrid composite, Materials Research. 18(2) (2015) 240-2444.
2. E. T.Salim, Rapid thermal oxidation for silicon nanocrystal based solar cell, International Journal of Nanoelectronics and Materials 5(2) (2012) 95-100.
3. J. L.R. Ferracane, composite state of the art. Dent Mater 27(1) (2011) 29- 38.
4. S. A. Naayi, A. I. Hassan, E.T. Salim, FTIR and X-ray diffraction analysis of Al2O3nanostructured thin film prepared at low temperature using spray pyrolysis method, International Journal of Nanoelectronics and Materials 11 (2018) 1-6.
5. N. Moszner, S. Klapdohr, Nanotechnology for Dental Composites. International Journal of Nanotechnology 1 (2004) 130-156.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献