The chemical reduction behavior of NiO under various carbon monoxide (CO) concentration as a reduction agent was studied. The NiO and Ni0 transformations were identified using TPR and XRD techniques. It was shown that, the completed reduction occurred at temperature 700 °C for 40% CO and 900 °C for 10% and 20% CO. During the chemical reduction process, nickel carbide was formed at temperature 400 °C and another formation of carbon amorphous appeared at 500 °C and proved through diffraction of XRD pattern at 2θ: 22.86 under 20% CO/N2 and and 2θ: 26.15 under 40% CO/N2. The interpretation of physisorption data showed that the pore size after reduction with various CO concentration comprised as microporous size in the range of 6-40 nm. Therefore, CO as a mild reduction agent stated that as the concentration of CO high, the rate of reduction affected and formed a very crystalline of Ni0 particle.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference10 articles.
1. L. Petrov, Problems and Challenges About Accelerated Testing of the Catalytic Activity of Catalysts,, in Principles and Methods for Accelerated Catalyst Design and Testing, Dordrecht: Springer Netherlands, 2002, p.13–69.
2. European Nickel Institute, The Importance of Nickel Compounds: Catalyst,, (2007).
3. M. N. Abu Tahari et al., Influence of hydrogen and various carbon monoxide concentrations on reduction behavior of iron oxide at low temperature,, Int. J. Hydrogen Energy, p.1–9, (2018).
4. J. Moon and V. Sahajwalla, Investigation into the Role of the Boudouard Reaction in Self-Reducing Iron Oxide and Carbon Briquettes,, vol. 37, no. April, p.215–221, 2006.N.
5. Dzakaria et al., Studies of Fe Metal Carburization by Carbon Monoxide Using XRD and TPR Techniques,, Mater. Sci. Forum, vol. 888, p.524–528, (2017).
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献