Abstract
The barium ferrite BaFe12O19 with c-plane anisotropy, which possessed relative high saturation magnetization and low coercivity, had been synthesized by hydrothermal method with different reaction time of 5 h, 8 h,11 h,14 h, and 17 h. The X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and vibrating sample magnetometer (VSM) were used to study the phase composition, microstructure and magnetic properties of barium ferrite, respectively. The results showed the intensities of the peak were enhanced and there was no impurity phase. With the prolonging of the reaction time to 11 h, 14 h and 17 h, the grain size increased, and the equivalent diameter was about 1 μm, and the thickness was about 100 nm. When the reaction time was 17 h,the coercivity of barium ferrite was 1104 Oe. The reduction of coercivity was ascribed to the increase of particle size and the reduction in magnetic anisotropy.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献