Impact of the Co Doping on the Structure, Magnetic Properties, and Phase Transition in Ni50-xCoxMn38Sn12 Ribbons

Abstract

Three Heusler alloys, Ni50-xCoxMn38Sn12 (x = 1, 2, and 3), were elaborated by rapid solidification. The impact of the Co doping on the structure, magnetic properties, and phase transition in these alloys was studied. The structure of the Ni49Co1Mn38Sn12 and Ni48Co2Mn38Sn12 ribbons was martensite 14M monoclinic structure, while the Ni47Co3Mn38Sn12 sample structure was austenite cubic L21. The thermal analysis showed the impact of the substitution Ni by Co. It was noted that the temperatures of martensitic transition moved lower, and a decreases progressively of enthalpy and entropy changed. Likewise, an obvious increase in the temperature of Curie transition for austenite phase (TAC) was observed and a jump of magnetization change (ΔM) was detected, with increasing Cobalt content.