Abstract
A 300-metric ton converter in a steel plant in China was studied. The influence of factors such as slag composition and temperature in the smelting process on the dephosphorization effect was statistically analyzed. The dephosphorization ability of slag increased firstly and then decreased with the increase of temperature, basicity and FeO content. Low-temperature, high-basicity and high-oxidizing slag are thermodynamically beneficial to promote the dephosphorization reaction, but the basicity is higher than 4.0, and the temperature is higher than 1640 °C are not conducive to the slag to obtain better fluidity. At the same time, too high FeO content will increase the activity coefficient of P2O5, thereby increasing its activity, which is not conducive to the progress of the dephosphorization reaction. As the end point content of carbon decreases, the oxygen content increases and the phosphorus content decreases. A very low carbon content is not conducive to metal yield and temperature control.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference19 articles.
1. Jiang M F, Cui Y Y, Wang D Y, et al. Effect of Modification Treatment for Reduction of Dephosphorization Slag in Hot Metal Bath[J]. Journal of Iron and Steel Research International, 2013, 20(1):1, 20-6, 20.
2. Wang Y M, Tao L, Guo H Y, et al. Dephosphorization influence factors in converter hot metal pretreatment[J]. Iron and Steel, 2020, 55(9):29.
3. Yang X, Matsuura H, Tsukihashi F.Reaction behavior of P2O5 at the interface between solid 2CaO-SiO2 and liquid CaO-SiO2-FeOx-P2O5 slags saturated with solid 5CaO·SiO2·P2O5 at 1573 K[J]. ISIJ International, 2010, 50(5):702.
4. Zhao X, Song Q, Wang T Y. Enlightenment of the reorganization and collaboration of Nippon Steel Corporation and Sumitomo Metal Industries, Ltd. for Chinese steel industry[J]. China Metallurgy, 2015, 25(12):1.
5. Yoshida K, Yamazaki I, Tozaki Y, et al. Development of effective refining process consisting of both hot metal pretreatment and decarburization in two top and bottom blown converter[J]. Tetsurto-Hagane, 1990, 76(11):1817.