Abstract
The thermal barrier coatings (TBC) are commonly used for protection of jet engine parts. In presented article the influence of chemical composition of TBCs bond coats on isothermal oxidation resistance was analysed. The bond coat was plasma sprayed (APS) using different MCrAlY alloys produced by Oerlikon-Metco: Metco 4451, AMDRY 997, AMDRY 962, AMDRY 365-1, AMDRY 995C. The conducted research showed big difference in coating thickness despite the same spraying parameters. The difference in porosity was not observed. The isothermal oxidation test was conducted during 500h at 1100°C in static laboratory air. The obtained results showed, that degradation mechanism of MCrAlY bond coats regardless of chemical composition is similar. The formation of scale contained aluminium and chromium oxides was observed. The internal oxidation effect was also observed in produced coatings.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference18 articles.
1. L. Swadźba, A. Maciejny, B. Formanek, et al., Microstructure and resistance to cracking of modified Al-Si and Al-Cr diffusion coatings on ŻS6K nickel-based superalloys, Surf. and Coat. Techn., 54-55 (1992), 84-90, https://doi.org/10.1016/S0257-8972(09)90032-9.
2. M. Pytel. M. Góral, M. Maliniak, The influence of production method on oxidation resistance of the aluminide coatings obtained on IN 100 alloy, Arch. of Mat. Science and Eng., 53 (2012) 2, 102-108.
3. M. Pytel, T. Tokarski, M. Góral, R. Filip, Structure of Pd-Zr and Pt-Zr modified aluminide coatings deposited by a CVD method on nickel superalloys, Kov. Mat., 57(2019) 5, 343-354.
4. K.A. Unocic, C.M. Parish, B.A. Pint, Characterization of alumina scale formed on coated and uncoated doped alloys, Surf. and Coat. Technol, 206 (2011), 1522-1528.
5. W. Nowak, Naumenko D., Mor G., et al., Effect of processing parameters on MCrAlY bondcoat roughness and lifetime of APS-TBC systems, Surf. and Coat. Technol., 260 (2014), 82-89, 10.1016/j.surfcoat.2014.06.075.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献