SiC/0~20% graphite (volume fraction) composites were successfully fabricated by pressureless sintering at 1700 °C for 2 h in nitrogen atmosphere. The impregnating and heat treatment process for the samples with silica sol/phenolic impregnant was carried out at 1450 °C for 2 h in nitrogen atmosphere. The Vickers hardness, oxidation resistance and thermal shock property of the composites before and after treatment were tested, and the microstructure and phase composition were characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD). The results shown that the Vickers hardness of SiC/20% graphite was increased from 3.35 GPa to 4.90 GPa by heat treatment, and the oxidation resistance and thermal shock property of the heat treated samples were also improved significantly. The SEM and XRD results revealed that the formation of new SiC particles by the reaction of silica sol and phenolic was the main reason for the mechanical properties improvements.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science