A pseudo-binary phase diagram of the (Bi,Pb)-Sr-Ca-Cu-O system along the Bi1.6Pb0.4Sr2Can-1CunOx line is constructed. This resulting phase diagram shows three kinds of peritectic reactions, one eutectic reaction and one peritectoid reaction. The equilibrium solid phases in this diagram are the 2201 (n=1), 2212 (n=2), 2223 (n=3) and (Sr,Ca)CuO2 (n→∝) phases. The 2201 phase is solid solution which is stable at 1≤n≤1.2. The eutectic composition point is close to the maximum solid solution composition of the 2201 phase. The temperature interval between the peritectic reaction of L + (Sr,Ca)2CuO3 + (Sr,Ca)CuO2 → 2212 and the eutectic reaction of L → 2201 + 2212 is only about 3°C. For the composition of n=3, CaO and the liquid phase are stable at temperatures above 940°C. During the cooling, these two phases react peritectically to (Sr,Ca)2CuO3. At around 890°C, (Sr,Ca)2CuO3 reacts with the liquid to produce (Sr,Ca)CuO2. At around 865°C, (Sr,Ca)2CuO3 and (Sr,Ca)CuO2 react with the liquid to produce the 2212. The 2223 phase is transformed by a peritectoid reaction of the 2212 phase and residual (Sr,Ca)2CuO3, (Sr,Ca)CuO2.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference11 articles.
1. H. Meada, Y. Tanaka, M. Fukutomi and T. Asano: Japan. J. Appl. Phys. 27 (1988), p.209.
2. R. S. Roth, C. J. Rawn, B. P. Burton and F. Beech: M.A. Green: J. Res. Nat. Inst. Stand. Technol. 95 (3) (1990), p.291.
3. K. Schulze, P. Majewski, B. Hettich and G. Petzow: Z. Metallk. 81 (1990), p.836.
4. Y. Ikeda, H. Ito, S. Shimomura, Y. Oue, K. Inaba, Z. Hiroi and M. Takano: Physica C 159 (1989), p.93.
5. C. J. Rawn, R. S. Roth, B. P. Burton and M. D. Hill: J. Am. Ceram. Soc. 77 (1994), p.2173.