Development of creep-resistant 8mol% Yttria-stabilized Zirconia (YSZ) ceramic has received much interest due to its potential use in fuel cells and thermal barrier coatings. In this research, Spark Plasma Sintering was used to develop a high-density 10 mol% La203 + YSZ composite. Compressive creep testing was performed at 1300 oC at 45 – 78 MPa load. The mechanism of plastic deformation of the composite was studied using Scanning Electron Microscopy and X-Ray Diffraction. The results suggest that lattice diffusion and grain boundary sliding were the active creep mechanisms.