Abstract
Polypropylene pre-oriented multifilament were made by melt spinning with fast winding, and then hard elastic polypropylene fibers were made followed by annealing treatment under some conditions. The effects of the conditions of melt spinning and annealing process on the elasticity of polypropylene fibers were studied. The structure and property of hard elastic polypropylene fibers were analyzed by DSC,WAXD,SAXS and Sound velocity anisotropy. The results showed that the hard elasticity of annealed fibers increased with the improving of speed of winding, and the elasticity also increased with the improving of annealing temperature and extension of annealing time, and the elastic recovery rate of PP multifilament can be as high as 93.6%. The crystal phase of unannealed and annealed PP fibers did not change. Annealing leaded to form perfectly the characteristic crystalline structure of crystals of being perpendicular to fiber axis.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference16 articles.
1. T. Joseph Donatien Leo, British Patent GB962, 231. (1964);
2. A. Boltniew, U.S. Patent 3, 323, 190. (1967).
3. B.S. Sprague, Relationship of structure and morphology to properties of hard, elastic fibers and films, J. Macromol. Sci. Part B: Polys. 8 (1973) 157-187.
4. H.D. Noether and W. Whitney, X-ray diffraction and morphology of crystalline, hard, elastic materials, Colloid Polym. Sci. 251 (1973) 991-1005.
5. M. Miles, J. Petermann and H. Gleiter, Structure and deformation of polyethylene hard elastic fibers, J. Macromol. Sci. Part B: Polys. 12 (1976) 523-534.