Eco-cement produced from waste concrete was proved to be feasible in early research. The seed crystal of ground granulated blast furnace slag (GGBS) was utilized in this research to lower the sintering temperature of eco-cement clinker. The mineral compositions of clinker with GGBS seed crystal was analyzed by X-ray diffraction (XRD), and the mechanical properties of eco-cement with GGBS seed crystal was also tested. Four main cement minerals were all observed in eco-cement clinker and the compressive strength of the eco-cement pastes can approach to about 66 MPa at 28 curing days. The results showed that GGBS seed crystal was favourable for the formation of cement minerals at a lower temperature. It can help reduce by about 50~100°C for the sintering process of cement clinker. Content of GGBS seed crystal should better be in the rage of 5%~8%, and the suitable sintering temperature should be 1350°C.
Publisher
Trans Tech Publications, Ltd.
Reference13 articles.
1. Jianzhuang Xiao. Recycled concrete (In Chinese)[M]. China Architecture & Building Press. (2008).
2. Enric Vázquez, Charles F. Hendriks, Gabriëlla M.T. Janssen. PRO40：International RILEM Conference on the Use of Recycled Materials in Buildings and Structures (Volume 2) RILEM Publications, (2004).
3. Castellote M, Alonso C, Andrade C, Turrillas X, Campo J. Composition and microstructural changes of cement pastes upon heating, as studied by neutron diffraction. Cem Concr Res 2004; 34(9): 1633–44.
4. Handoo SK, Agarwal S, Agarwal SK. Physical–chemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cem Concr Res 2002; 32(7): 1009–18.
5. Zhonghe Shui, Dongxing Xuan, Huiwen Wan, Beibei Cao. Rehydration reactivity of recycled mortar from concrete waste experienced to thermal treatment. Construction and building materials. 22 (2008) 1723-1729.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献