Affiliation:
1. Beijing Institute of Technology
Abstract
Hf6Ta2O17 ceramic powder was prepared by solid state reaction at 1600°C for 10 hours. The phase and microstructure of Hf6Ta2O17 ceramics were observed. The XRD results revealed that the sintered sample of the ceramic powder had single phase and the SEM results showed that the sintered sample was comparative dense. The thermal conductivity of the sintered sample was investigated and the value was comparative low.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference8 articles.
1. C. H. Liebert, R. A. Mlller J. Ame. Chem. Soc, Vol. 23 (1984), p.344.
2. X.Q. Cao, R. Vassen, D. Stoever. J. Eur. Ceram. Soc., Vol. 24 (2004), p.1.
3. L. Xie, M.R. Dorfman, A. Cipitria et al. J. Ther. Spr. Tec., Vol. 16 (2007), p.804.
4. M. R. Winter, D. R. Clarke. J. Ame Ceram Soc., Vol. 90 (2007), p.533.
5. H.S. Zhang, Q. Xu, F.C. Wang et al. J. Alloys & Compounds, Vol. 475 (2009), p.624.
Cited by
23 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献