The insitu-fabrication of TiCN ceramic coating by laser cladding-laser nitriding technique (LC-LN) was investigated. Pulsed YAG laser with the power of 500W was used as radiation source. Highly pure N2 was selected as the nitriding element; Titanium powder whose size is 20 m and the pure carbon powder were utilized as the coating materials. The influence of technology parameters such as pulse width, pulse frequency and scanning speed etc. on the insitu-formation of TiCN ceramic coating was studied. XRD results show that the main phases of the coating are TiC0.3N0.7 (or TiC0.2N0.8),TiN and TiN0.3. It was revealed that the appropriate process parameters for insitu-fabrication are the pulse frequency 15 Hz, pulse width 3.0ms, the scanning speed in the range of 9cm/min to 12cm/min, the pressure of N2 0.4MPa. The result of OM showed a metallurgical bonding without crack and bubble between the coating and the substrate was obtained. The microstructure of cladded coating is characterized by fine dentrites. The average microhardness in the coating is more than 1300HV which is about 4 times of that in the substrate.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference15 articles.
1. M. Van Stappen, L.M. Stals and M. Kerkhofs: Surf. Coat. Technol. Vol. 74-75 (1995), p.629.
2. F. Seidel, H.R. Stock and P. Mayr: Surf Coat Tech, Vol. 108-109 (1998), p.271.
3. E.I. Meletis: J. Mater. Eng. Vol. 11 (1989), p.159.
4. W.D. Sprou and R. Rothstein: Thin Solid Films Vol. 126 (1985), p.257.
5. L.E. Toth: Transition Metal Carbides and Nitrides, Academic Press, New York, 1971, p.165.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献