In this study, the fatigue crack growth rates (FCGRs) of Ti-15V-3Cr-3Al-3Sn alloy aged in the temperature ranges from 426 to 593 oC for 8 hrs was determined at stress ration of 0.1 or 0.5. The results of fatigue crack growth tests revealed the FCGRs decreased with increasing aging temperature. Generally, the 426oC aged specimen had the highest FCGRs among the specimens being tested, regardless of stress ratio. It was noted obvious increase in FCGRs occurred for the 482oC aged specimen at stress ratio of 0.5. Fatigue fracture appearance of various specimens tested in air exhibited predominantly transgranular fatigue fracture with coarse stripes for the specimens aged at/above 538oC. Intergranular fracture was more likely to be found in the 426oC aged specimen, and for the A482 specimen tested at high stress ratio.
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. P. J. Bania, G. A. Lenning, and J. A. Hall, Beta Titanium Alloys in the 1980's, (1983)209-229.
2. N. Niwa, T. Demura and K. Ito, ISIJ, 30(1990) 773-779.
3. J. Ma and Q. Wang, Mat. Sci. Eng., A243(1998)150-154.
4. Y. Kawabe and S. Muneki, ISIJ, 31(1991)785-791.
5. T. Inaba, K. Ameyama and M. Tokizane, ISIJ, ISIJ, 31(1991)792-798.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献