Abstract
An Fe-6.2wt%Si as-cast strip with equiaxed grains and obvious {001} fiber texture was produced by twin-roll strip casting process. The as-cast strip was successively performed by hot rolling, warm rolling and annealing. The microstructure and texture evolution at each process stage were investigated by using electron backscatter diffraction and x-ray diffraction. It was found that the finally annealed sheet was characterized by large grain size, mild γ-fiber texture and obvious {001} fiber texture. Therefore, a high magnetic induction and a low core loss were obtained in the sheet.