Abstract
In the present study, microstructure investigation of aluminide coatings after platinum modification deposited by CVD method on Inconel 713 LC Ni-base superalloys were performed. The platinum coatings 3 and 7 m thick were deposited by electroplating process. The diffusion treatment of platinum electroplating coatings at the temperature 1050 °C was carried out for 2h. The low-activity CVD aluminizing of heat treated coatings at the temperature 1050 °C was conducted for 8 h. On the grounds of the obtained results it was found that microstructure of diffusion treated platinum electroplating coatings 3 m and 7 m thick consisted of two phases: γ-Ni and (Al0.25Pt0.75)Ni3. The low activity CVD aluminizing of diffusion treated platinum electroplating coatings 3 and 7 m thick enables the diffusion coating obtaining. The main constituent of aluminide coatings was (Ni,Pt)Al phase.
Publisher
Trans Tech Publications, Ltd.
Reference13 articles.
1. M. Hetmańczyk, L. Swadźba, B. Mendala: Advanced materials and protective coating in aero-engines application, Journal of Achievements In Materials and Manufacturing Engineering 24/1 (2007) 372-381.
2. A. Hernas: High temperature creep resistance of steel and alloys, Silesian University of Technology Press, Gliwice, (2000).
3. J. Sieniawski: Nickel and titanium alloys in aircraft turbine engines, Advances in Manufacturing Science and Technology, 27 (2003) 3, 23-34.
4. J. Haynes1, K. More, B. Pint, I. Wright, K. Cooley1, Y. Zhang: Effects of Platinum Additions on the Adherence of Alumina Scales to CVD Aluminide Bond Coatings, High Temperature Corrosion and Protection of Materials 5 (2000).
5. F. Pedraza, A. Kennedy, J. Kopecek, P. Moretto: Investigation of the microstructure of platinum-modified aluminide coatings, Surface & Coatings Technology 200 (2006) 4032– 4039.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献