Research on High Performance Vitrified Bond Diamond Wheel-Reference-Cited by-同舟云学术

Research on High Performance Vitrified Bond Diamond Wheel

Published:2012-04 Issue: Volume:497 Page:83-88
ISSN:1662-8985
Container-title:Advanced Materials Research
language:
Short-container-title:AMR

Author:

Liu Yi Bo¹,Liu Wei¹,Huang Xia¹,Zhang Hai Peng¹

Affiliation:

1. Beijing Gang Yan Diamond Products Company

Abstract

Two kinds of vitrified bonds, bond L (low temperature bond) and bond G (high strength bond), were blended by ball-milling in producing diamond wheels. Proper Sintering techniques were employed by analyzing properties of the wheel through DSC testing and fracture strength. The wheels were applied in machining PDC in comparison with similar product on market. It showed that the blended bond reached its highest fracture strength when bond L amount was about 20wt~24wt%; combination of this two kinds of vitrified bonds would improve the wheel’s comprehensive properties by raising its fracture strength to 89MPa when bond L takes up 22wt%; service life of wheels prepared by this blended bond was 30~50% longer than similar market product and efficiency improved by more than 20%.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Link

https://www.scientific.net/AMR.497.83.pdf

Reference5 articles.

1. US Patent. US6454027 B1; Anthony Griffo, ect. Polycrystalline diamond carbide composites.

2. Volkmar Richter. Metal Powder Report, 2006, 61 (11).

3. Hongxia Zhang, Gaimin Wang，Yong Hua. China Ceramic, 2003, 39(1): 38~40 (in Chinese).

4. Yuanjiang Zhang, Dingliang Wei. Precise Manufacture and Automation, 1996(3): 23~24 (in Chinese).

5. Zhejiang University etc. Silicate Physical Chemistry. Beijing: China architecture & building press, 1980 (in Chinese).