Mechanical Properties of Hydroxyapatite Ceramic Prepared from Micropowder and Nanopowder

Abstract

In this work, hydroxyapatite ceramics were prepared from hydroxyapatite micropowder and nanopowder. The hydroxyapatite nanopowder was obtained from natural buffalo bone by using a high speed vibro-milling machine for 2 hour. The green compacted pellets of all HA powders were subsequently sintered at 1200, 1250, 1300 and 1350°C for 3 hour and then the physical and mechanical characterizations as well as microstructural evaluation have been carried out. It was found that the optimum sintering temperature were 1250°C by fabricated from nanopowder which gave the HA nanoceramic with the maximum bending strength of 78.6±2.6 MPa. This is about 200% higher than that of the sample which fabricated from HA micropowder.