Abstract
Abstract
We prepared crystals of (C6H5C
n
H2n
NH3)2PbBr4 (n = 2, 3, 4), and evaluated their photoluminescence and scintillation characteristics. According to the photoluminescence spectra under 340 nm excitation light, a photoluminescence peak at around 410 nm due to free exciton emissions appeared in (C6H5C2H4NH3)2PbBr4 (2PEA), (C6H5C3H6NH3)2PbBr4 (3PPA) and (C6H5C4H8NH3)2PbBr4 (4PBA). The quantum efficiencies of 2PEA, 3PPA and 4PBA were 0.24, 0.01 and 0.04, respectively. In scintillation, a sharp scintillation peak originating from the exciton emissions was detected at approximately 436 nm for 2PEA, 459 nm for 3PPA and 442 nm for 4PBA. In addition, the scintillation light yield of 4PBA under 59.5 keV gamma-ray irradiation from 241Am was determined to be approximately 2200 photons MeV−1 in comparison with the yield of 2PEA (14 000 photons MeV−1), whereas the yield of 3PPA could not be determined due to its low scintillation intensity.
Subject
General Physics and Astronomy,Physics and Astronomy (miscellaneous),General Engineering
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献