Photoluminescence and scintillation properties of Pr-doped (Lu, Y)2Si2O7 crystals

Abstract

Abstract Pr-doped (Lu1−x , Y x )2Si2O7 (x = 0.25, 0.5, and 0.75) crystals were synthesized by the floating zone method. Emission peaks due to 5d–4f transitions of Pr3+ were observed at 300 nm under excitation of both UV light and X-rays. Scintillation decay times of 19–22 ns were obtained, and they originated from the 5d–4f transitions of Pr3+. Afterglow levels became high from 64.7 to 541 ppm as the Y-admixed concentration increased. The light yields were estimated to be 560–700 photons MeV−1 by comparing the channels of photoabsorption peaks from the pulse height spectra of 137Cs γ-rays measured using prepared crystals and commercial Gd2SiO5 reference.