Corrosion Protection of Aluminum Alloy 2024-T3 by Vanadate Conversion Coatings

Author:

Guan H.1,Buchheit R. G.1

Affiliation:

1. 1Fontana Corrosion Center, Department of Materials Science and Engineering, The Ohio State University, Columbus, OH 43210.

Abstract

Abstract In this paper, the formation, chemistry, morphology, and corrosion protection of a new type of inorganic conversion coating is described. This coating, referred to as a vanadate conversion coating (VCC), forms on aluminum alloy substrates in a matter of minutes during simple immersion in aqueous vanadate-based solutions at ambient temperatures. VCCs are yellow in color and conformal across the surface of aluminum alloy 2024-T3 (AA2024-T3 [UNS A92024]) substrates. Auger electron sputter depth profiles and x-ray absorption near-edge spectroscopy show that VCCs formed by a 3-min immersion are 300 nm to 500 nm thick and consist of a mixture of vanadium oxides and other components in the coating bath. In anodic polarization experiments conducted in aerated chloride solutions, VCCs increase the pitting potential and decrease the rate of oxygen reduction. When characterized by electrochemical impedance spectroscopy, VCCs demonstrate a low-frequency impedance between 1 MΩ-cm2 and 2 MΩ-cm2 after 24 h exposure to aerated 0.5 M sodium chloride (NaCl) solutions. In salt spray testing conducted according to ASTM B117, VCCs suppress formation of large pits for more than 168 h. VCCs also appear to be self-healing. Analysis of solution in contact with VCCs by inductively coupled plasma emission spectroscopy indicates that vanadate is released into solution upon exposure. Vanadium deposits were identified by x-ray microchemical analysis on a bare alloy substrate held in close proximity to a vanadate conversion-coated surface, and corrosion resistance of this bare surface was observed to increase during exposure. An important component of VCC formation appears to involve inorganic polymerization of V5+, which leads to the buildup of a film that passivates the surface and inhibits corrosion.

Publisher

NACE International

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Cited by 115 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3