Author:
Bessmertnyi V. S.,Zdorenko N. M.,Min’ko N. I.,Bondarenko M. A.,Vorontsov V. M.,Cherkasov A. V.,Makarov A. V.,Varfolomeeva S. V.
Abstract
The technology of facing material based on mechanically activated cullet modified with sodium hydroxides has been developed. The phase composition, macro- and microstructure of the lining material are investigated. It is established that the microstructure of a composite modified with sodium hydroxide in the interpore space is represented by lamellar crystals of sodium meta-, di- and orthosilicates. The optimal composition for obtaining a facing material with a compressive strength of 24.7 MPa and a softening coefficient of 0.91 has been established.
Publisher
Izdatel'skii dom Spektr, LLC
Reference20 articles.
1. Минько Н. И., Добринская О. А. Технологические особенности использования стеклобоя в производстве стекломатериалов // Техника и технология силикатов, 2019. Т. 26, № 1. C. 9 – 14.
2. Минько Н. И., Добринская О. А., Булгаков А. С. Технологические особенности использования вторичных продуктов в производстве силикатных материалов // Физика и химия стекла. 2018. Т. 44, № 3. C. 308 – 314.
3. Зайцева Е. И. Строительные безобжиговые композиты на основе боя технических стекол // Российский химический журнал. 2003. Т. 47, № 4. С. 26 – 31.
4. Гольцман Б. М., Яценко Е. А., Геращенко В. С. и др. Пористые теплоизоляционные материалы на основе различных видов силикатного сырья // Изв. высших учебных заведений. Северо-Кавказский регион. Технические науки. 2020. № 1(205). C. 55 – 60.
5. Шабельская Н. П., Яценко Е. А., Медведев Р. П. и др. Применение пеностекла на основе золошлаковых отходов и стеклобоя для получения каталитически активных композиций // Неорганические материалы. 2020. Т. 56, № 7. С. 808 – 812.