Abstract
A dense-sintered protoenstatite ceramics based on fluorinated talc was obtained. Influence of BaO and Al2O3 additives on the sinterability, structure and strength of ceramics was investigated. It makes possible to reduce the sintering temperature to 1225 – 1250 °C due to formation of glassy phase. Additive of ZnO intensifies solid phase sintering at 1320 °C.
It significantly improves compressive strength of ceramics up to 660 MPa that exceeds the strength of traditional steatite materials by 3 times.
Publisher
Izdatel'skii dom Spektr, LLC
Reference17 articles.
1. Kamutzki F., Schneider S., Barowski J., et al. Sili-cate dielectric ceramics for millimeter wave applications // J. of the European Ceramic Society. 2021. V. 41. P. 3879 – 3894. DOI: 10.1016/j.jeurceramsoc.2021.02.048.
2. Song K. X., Chen X. M., Fan X. C. Effects of Mg/Si Ratio on Microwave Dielectric Characteristics of Forsterite Ceramics // J. of the American Ceramic Society. 2007. V. 90, No. 6. P. 1808 – 1811. DOI: 10.1111/J.1551-2916.2007.01656.X.
3. Song M. E., Kim J. S., Joung M. R., et al. Synthesis and Microwave Dielectric Properties of MgSiO3 Ceramics // J. of the American Ceramic Society. 2008. V. 91, No. 8. P. 2747 – 2750. DOI: 10.1111/J.1551-2916.2008.02499.X.
4. Химическая технология керамики / ред. И. Я. Гузман. М.: ООО РИФ «Стройматериалы», 2003. 496 с.
5. Верещагин В. И. Физико-химические критерии оценки и прогнозирования действия модифицирующих добавок в силикатных и оксидных системах // Известия Томского политехнического университета. 2000. Т. 303, Вып. 1. С. 225 – 229.