Effects of carbodiimide combined with ethanol–wet bonding pretreatment on dentin bonding properties: an in vitro study

Abstract

Purpose This study evaluated the combined effects of Carbodiimide (EDC) and ethanol–wet bonding (EWB) pretreatment on the bond strength and resin–dentin surface. Methods Phosphoric acid-etched dentin specimens were randomly divided into five groups based on the following pretreatments: deionized water (control), EWB, 0.3M EDC in water (EDCw), EDC water solution combined EWB (EDCw + EWB), and 0.3M EDC in ethanol (EDCe). A scanning electron microscope (SEM) was used to observe the morphology of collagen fibrils on the demineralized dentin matrix in each group after pretreatment. The adhesives Prime & Bond NT (PB) (Dentsply De trey, Konstanz, Germany) or Single bond 2 (SB) (3M ESPE, St. Paul, MN, USA) was applied after pretreatments, and a confocal laser scanning microscope (CLSM) was used to evaluate the quality of resin tags. The degree of conversion (DC) of the adhesive was investigated by Fourier transform infrared spectroscopy (ATR-FTIR). The dentin was first bonded with resin and bathed in water at 37 °C for 24 h. Half of them were subjected to 10, 000 cycles in a thermocycler between 5 °C and 55 °C before a microshear bond strength (µSBS) test. The statistical methods were Analysis of Variance (ANOVA) and a Tukey post hoc test at α = 0.05. Results The µSBS was significantly affected by pretreatments (p < 0.001), adhesives (p < 0.001), and aging conditions (p < 0.001) as revealed by the three-way ANOVA. The EDCw, EDCw + EWB, and EDCe groups significantly increased the µSBS; the EDCw + EWB and EDCe groups produced the highest µSBS. In the EDC-containing groups, the SEM showed at the collagen fibrils in the dentin matrix formed a three-dimensional network structure in the tubules after cross-linking into sheets, and the hybrid layer formed thicker resin tags under a CLSM. In the EDC-containing groups, the CLSM observed an increase in the length of resin tags. PB showed a higher DC and bonding strength than SB, and the five pretreatment groups tested did not affect the DC of the two adhesives. Conclusions In etch–and–rinse bonding system, EDC combined with EWB pretreatment can improve the quality of the hybrid layer and enhance the mechanical properties of demineralized dentin matrix. Pretreatment with EDC–ethanol solution may be a new clinically friendly option for enhancing dentin bonding durability.