Effects of Different Laser Treatments on Some Properties of the Zirconia-Porcelain Interface

Author:

Abdulsatar Abdulsatar M1,Hussein Basima M A1ORCID,Mahmood Ali M1

Affiliation:

1. Institute of Laser for Postgraduate Studies, University of Baghdad, Baghdad, Iraq

Abstract

Introduction: This study was performed to compare the effect of Fractional CO2 laser or Q switched Nd:YAG laser of surface treatment on the shear bond strength of zirconia-porcelain interface. Methods: Fractional CO2 laser at 30 W, 2 ms, time interval 1 ms, distance between spots 0.3 mm, and number of scans is (4) or Q switched Nd:YAG laser at 30 J/mm2 and 10 Hz were used to assess the shear bond strength of zirconia to porcelain. Pre-sintered zirconia specimens were divided into three groups (n = 10) according to the surface treatment technique used: (a) untreated (Control) group; (b) CO2 group; (c) Nd:YAG group. All samples were then sintered and veneered with porcelain according to the manufacturer’s instructions. Surface morphology was examined using a light microscope, the surface roughness test was done by the atomic force microscope (AFM), and the shear bond strength (SBS) test was done by a universal testing machine. After debonding following shear bond test, zirconia surfaces were examined under a light microscope to determine their fracture mode. Results: The Results of this study showed that the lowest SBS was recorded in the control group, and the highest SBS recorded in the Fractional CO2 group, followed by the Q switched Nd:YAG laser group, as well as an increase in surface roughness and change in the morphology and mode of failure in the experimental groups . Conclusion: This study shows that Fractional CO2 laser and Q switched Nd:YAG laser treatments significantly increase the bond strength than untreated zirconia .

Publisher

Maad Rayan Publishing Company

Subject

Urology,Nephrology,Dermatology,Dentistry (miscellaneous),Orthopedics and Sports Medicine,Surgery

Cited by 8 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3