SPECIFIC FEATURES OF THE CURRENT FLOW THROUGH AN ALUMINA-BASED METAL-CERAMIC COMPOSITE DURING ELECTRON BEAM IRRADIATION IN THE FOREVACUUM PRESSURE RANGE-Reference-Cited by-同舟云学术

SPECIFIC FEATURES OF THE CURRENT FLOW THROUGH AN ALUMINA-BASED METAL-CERAMIC COMPOSITE DURING ELECTRON BEAM IRRADIATION IN THE FOREVACUUM PRESSURE RANGE

Published:2024 Issue:1 Volume:28 Page:47-53
ISSN:1093-3611
Container-title:High Temperature Material Processes An International Quarterly of High-Technology Plasma Processes
language:en
Short-container-title:High Temp Mat Proc

Author:

Zenin Aleksey A.,Bakeev I. Yu.,Klimov A. S.,Oks Efim M.,Tyunkov Andrey V.

Abstract

We describe some specific features of the current passage through an Al2O3-Ti metal-ceramic composite sample during irradiation by a forevacuum-pressure plasma-cathode electron beam source. The composition ratio of the composite was 90% Al2O3 and 10% Ti by weight. It is shown that during electron-beam irradiation, the magnitude and direction of the current through the sample depend on the temperature as well as on the sintering time at given temperature. The absolute value of the recorded current can reach 15 mA for an electron-beam current of 60 mA and electron energy of 10 keV. The dependence of the current is caused by redistribution of titanium over the depth of the sintered composite during heating, and provides a means for forming gradient metal-ceramic materials with variable content of components over the depth.

Publisher

Begell House

Link

https://www.dl.begellhouse.com/download/article/5181a26855785086/HTM-48461.pdf

Reference23 articles.

1. Abyzov, A.M., Aluminum Oxide and Alumina Ceramics (Review). Part 1. Properties of Al2O3 and Commercial Production of Dispersed Al2O3, Refractories Indust. Ceram., vol. 60, pp. 24-32, 2019.

2. Burdovitsin, V.A., Medovnik, A.V., Oks, E.M., Skrobov, E.V., and Yushkov, Y.G., Potential of a Dielectric Target during Its Irradiation by a Pulsed Electron Beam in the Forevacuum Pressure Range, Tech. Phys., vol. 57, no. 10, pp. 1424-1429, 2012.

3. Flinn, B.D., Ruhle, M., and Evans, A.G., Toughening in Composites of Reinforced with Al, Acta Metall., vol. 37, no. 11, pp. 3001-3006, 1989.

4. Katz, J.D., Microwave Sintering of Ceramics, Ann. Rev. Mater. Sci., vol. 22, no. 1, pp. 153-170, 1992.

5. Klimov, A.S., Burdovitsin, V.A., Zenin, A.A., Oks, E.M., Khasanov, O.L., Dvilis, E.S., and Khasanov, A.O., Specific Features of the Charge Neutralization of Silicon Carbide in Sintering by Electron Beam in the Forevacuum Range of Pressures, Tech. Phys. Lett., vol. 41, no. 8, pp. 747-749, 2015.