Composition Dependent Electrical Properties of (Ba1−xCaxZr0.1Ti0.9)O3 Ceramics, Near Morphotropic Phase Boundary (0.140 ≤ x ≤ 0.160)

Abstract

In this work, pellet samples of (Ba1−xCaxZr0.1Ti0.9)O3, (0.140 ≤ x ≤ 0.160) were prepared using solid-state reaction route with double sintering. The dielectric and structural properties of the prepared samples were measured, from room temperature to 250 °C, at different frequencies, in the range 10–1000 KHz. A peak shifting anomaly in the X-ray diffraction peaks patterns, an anomalous change in the slope of c/a vs x plot, and the observed minimum values of dielectric constant, loss and conductivity of the prepared compositions show a strong compositional dependent dielectric and structural properties, indicating a morphotropic phase transition type behavior, at the composition with x = 0.150.