The effect of rolling direction and strain rates on the tensile properties of AA2024-T3 aluminum alloy

Author:

Demirdöğen Mehmet FatihORCID,Kılıç Süleyman1ORCID

Affiliation:

1. AHİ EVRAN ÜNİVERSİTESİ

Abstract

The AA2024-T3 alloy is a lightweight and durable material commonly used in the aerospace industry. This study investigates the impact of the rolling direction (RD) and strain rates on the alloy’s tensile properties. Tensile tests have been performed on samples oriented parallel and transverse to the rolling direction at varying strain rates (5, 25, and 125 mm/min). Samples parallel to the rolling direction have exhibited higher strength compared to those in the transverse direction (TD). At a strain rate of 5 mm/min, the maximum tensile strength in RD samples has been 530.72 MPa, while in TD samples, it has been 505.76 MPa. At 25 mm/min, the tensile strength has been 498.31 MPa in RD and 482.91 MPa in TD. At 125 mm/min, the tensile strength has been 508.52 MPa in RD and 480.36 MPa in TD. The increase in strain rate has had a complex effect on the mechanical properties. The total elongation values have also varied with strain rate, with the highest total elongation observed at 5 mm/min (0.168) in both RD and TD directions. These findings have highlighted the significant impact of the rolling direction and strain rate on the mechanical properties of the AA2024-T3 alloy, which should be considered in design and manufacturing processes.

Publisher

European Mechanical Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3