Abrasive Wear Resistance of Nodular Cast Iron After Selected Surface Heat and Thermochemical Treatment Processes-Reference-Cited by-同舟云学术

Abrasive Wear Resistance of Nodular Cast Iron After Selected Surface Heat and Thermochemical Treatment Processes

Published:2024-07-19 Issue: Volume: Page:
ISSN:2299-2944
Container-title:Archives of Foundry Engineering
language:pl
Short-container-title:

Author:

Baron C.¹^ORCID,Stawarz M.¹^ORCID,Studnicki A.¹,Jezierski J.¹^ORCID,Wróbel T.¹^ORCID,Dojka R.²,Lenert M.¹²,Piasecki K.¹²^ORCID

Affiliation:

1. Silesian University of Technology, Department of Foundry Engineering, Towarowa 7, 44-100 Gliwice, Poland

2. Odlewnia RAFAMET Sp. z o.o., ul. Staszica 1, 47-420 Kuźnia Raciborska, Poland

Abstract

The article presents the test results on the technology of surface hardening of castings from unalloyed and low-alloy nodular cast iron using the method of surface heat treatment, i.e., induction surface hardening and methods of thermochemical treatment, i.e. gas nitriding, nitrocarburizing, and nitrocarburizing with oxidation. The scope of research included macro- and microhardness measurements using Rockwell and Vickers methods, respectively, as well as metallographic microscopic examinations using a light microscope. Furthermore, abrasive wear resistance tests were performed using the pin-on-disk method in the friction pair of nodular cast iron – SiC abrasive paper and the reciprocating method in the friction pair of nodular cast iron – unalloyed steel. Analysis of the test results shows that the size and depth of surface layer hardening strongly depend on the chemical composition of the nodular cast iron, determining its hardenability and its ability to create diffusion layers. Medium induction surface hardening made it possible to strengthen the surface layer of the tested nodular cast irons to the level of 700 HV0.5 with a hardening depth of up to approximately 4000μm, while various variants of thermochemical treatment provided surface hardness of up to 750 HV0.5 with a hardening depth of up to approximately 200μm. Furthermore, induction surface hardening increased the resistance to abrasive wear of nodular cast iron castings, depending on the test method, by an average of 70 and 45%, while thermochemical treatment on average by 15 and 60%.

Publisher

Polish Academy of Sciences Chancellery

Link

https://journals.pan.pl/Content/132159/AFE%203_2024_04.pdf

Reference1 articles.

1. [1] Pan, C., Gu, Y., Chang, J. & Wang, C. (2023). Recent patents on friction and wear tester. Recent Patents on Engineering. 17(4), 86-102. DOI:10.2174/1872212117666220621103655. [2] Yang, Z., Ye, S., Wang, Z., Li, Z. & Li. W. (2023). Experimental and simulation study on braking noise characteristics and noise reduction strategies of the friction pair between the SiCp/A356 brake disc and the synthetic pad. Engineering Failure Analysis. 145, 1-20, 107017. https://doi.org/10.1016/j.engfailanal.2022.107017. [3] Wang, K., Zhang, Z., Dandu, R.S.B. & Cai. W. (2023). Understanding tribocorrosion of aluminum at the crystal level. Acta Materialia. 245, 1-13, 118639. DOI:10.1016/j.actamat.2022.118639. [4] Jakobsen, P.D., Langmaack, L., Dahl, F. & Breivik. T. (2013). Development of the soft ground abrasion tester (SGAT) to predict TBM tool wear, torque and thrust. Tunneling and Underground Space Technology. 38, 398-408. DOI:10.1016/j.tust.2013.07.021. [5] Tiruvenkadam, N., Thyla, P.R. Senthil Kumar, M., Kader, N.A., Pradeep, V.K., Vishnu Kumar, R., Sasikumar, N. (2013). Development of multipurpose reciprocating wear tester under various environmental parameters. In International Conference on Energy Efficient Technologies for Sustainability, 10 – 12 April 2013 (pp. 213 – 216). Nagercoil, India. DOI:10.1109/ICEETS.2013.6533384. [6] Guanzhang, H., Xiaojing, Y., Yilin, C. & Jie, D. (2011). Development of a system for measuring the variation of friction force on reciprocating wear tester. In Third International Conference on Measuring Technology and Mechatronics Automation, 6-7 January 2011 (Vol. 1, pp. 1045-1049). DOI:10.1109/ICMTMA.2011.262. [7] Vasquez, H., Lozano, K., Soto, V. & Rocha, A. (2008). Design of a wear tester for nano-reinforced polymer composites. Measurement. 41(8), 870-877. DOI:10.1016/j.measurement.2007.12.003. [8] Wei, R., Wilbur, P.J., Sampath, W.S., Williamson, D.L., Qu, Y. & Wang, L. (1990). Tribological studies of ion-implanted steel constituents using an oscillating pin-on-disk wear tester. Journal of Tribology. 112(1), 27-36. DOI:10.1115/1.2920227. [9] Desale, G.R., Gandhi, B.K. & Jain, S.C. (2005). Improvement in the design of a pot tester to simulate erosion wear due to solid-liquid mixture. Wear. 259(1-6), 196-202. DOI:10.1016/j.wear.2005.02.068. [10] Wang, X., Song, Y., Li, C., Zhang, Y. Ali, H.M., Sharma, S., Li, R. et al. (2023). Nanofluids application in machining: a comprehensive review. International Journal of Advanced Manufacturing Technology. 131(5-6), 3113-3164. DOI:10.1007/s00170-022-10767-2. [11] De Stefano, M., Aliberti, S.M. & Ruggiero. A. (2022). (Bio) Tribocorrosion in dental implants: principles and techniques of investigation. Applied Sciences. 12(15), 1-16. DOI:10.3390/app12157421. [12] Vilhena, L., Ferreira, F., Oliveira, J.C. & Ramalho. A. (2022). Rapid and easy assessment of friction and load-bearing capacity in thin coatings. Electronics. 11(3), 1-19, 296. DOI:10.3390/electronics11030296. [13] Valigi, M.C., Logozzo, S. & Affatato, S. (2017). New challenges in tribology: wear assessment using 3d optical scanners. Materials. 10(5), 1-13, 548. DOI:10.3390/ma10050548. [14] Dwulat, R., Janerka, K. & Grzesiak, K. (2021). The influence of final inoculation on the metallurgical quality of nodular cast iron. Archives of Foundry Engineering. 21(4), 5-14. DOI:10.24425/afe.2021.138673. [15] Janerka, K., Kostrzewski, Ł., Stawarz, M. & Jezierski. J. (2020). The importance of sic in the process of melting ductile iron with a variable content of charge materials. Materials. 13(5), 1-10, 1231. DOI:10.3390/ma13051231. [16] Gumienny, G., Kurowska, B. & Fabian. P. (2020). Compacted graphite iron with the addition of Tin. Archives of Foundry Engineering. 20(3), 15-20. DOI:10.24425/afe.2020.133323. [17] Gunalan, M. & Anandeswaran, V.A. (2021). A holistic approach of developing new high strength cast iron for weight optimization. SAE Techical Paper. DOI:10.4271/2021-26-0244. [18] Bendikiene, R., Bahdanovich, A., Cesnavicius, R., Ciuplys, A., Grigas, V., Jutas, A., Marmysh, D., Nasan, A., Shemet, L., Sherbakov, S. & Sosnovskiy, L. (2020). Tribo-fatigue behavior of austempered ductile iron monica as new structural material for rail-wheel system. Medziagotyra. 26(4), 432-437. DOI:10.5755/j01.ms.26.4.25384. [19] [20] Zhu, Y., Keoleian, G.A. & Cooper. D.R. (2023). A parametric life cycle assessment model for ductile cast iron components. Resources, Conservation and Recycling. 189, 1-9, 106729. DOI:10.1016/j.resconrec.2022.106729. [20] Molian, P.A. & Baldwin, M. (1987). Effects of single-pass laser heat treatment on erosion behavior of cast irons. Wear. 118(3), 319-327. DOI:10.1016/0043-1648(87)90075-5. [21] Molian, P.A. & Baldwin. M. (1988). Wear behavior of laser surface-hardened gray and ductile cast irons. Part 2 erosive wear. Journal of Tribology. 110(3), 462-466. DOI:10.1115/1.3261651. [22] Wróbel, T., Studnicki, A., Stawarz, M., Baron, Cz., Jezierski, J., Bartocha, D., Dojka, R., Opiela, J. & Lisiecki, A. (2024). Improving the abrasion resistance of nodular cast iron castings by remelting their surfaces by laser beam. Materials. 17(9), 1-17, 2095. https://doi.org/10.3390/ma17092095.